Re: Heat balance at plane blade tip

William Duffield
Well, it's been over 50 years since I studied any thermodynamics or calculus, but your engineer's results agree with my intuition. I think they indicate that adjusting the chip breaker cap iron closer to the blade edge or refining its bottom surface for a larger contact area with the back of the blade or increasing its bevel angle to increase its thermal mass near the blade edge would all be ineffective at reducing the final temperature of the blade edge.

Messages In This Thread

Heat balance at plane blade tip
Re: Heat balance at plane blade tip
Re: Heat balance at plane blade tip
Re: Heat balance at plane blade tip
Re: Heat balance at plane blade tip
Re: Heat balance at plane blade tip
Re: Heat balance at plane blade tip
K&K SEM pictures
Re: K&K SEM pictures—here they are *LINK*
Re: K&K SEM pictures—here they are
Re: K&K SEM pictures
Re: K&K SEM pictures *LINK*
Re: K&K SEM pictures
The data shown above
Re: The data shown above
Re: The data shown above
Re: The data shown above
Re: Agree on three points
Question about setting blade exposure
Re: Question about setting blade exposure
Re: Question about setting blade exposure
Re: Question about setting blade exposure
Is planing the way to level this surface
Toothing planes
Gosh...
Re: Gosh...
Re: Gosh...
Re: Is planing the way to level this surface
Re: Question about setting blade exposure
Re: Question about setting blade exposure *PIC*
summary?
Re: summary?
Re: Question about setting blade exposure
A small experiment
Re: A small experiment
question
Re: question
clever setting procedure; blurring? *PIC*
Re: clever setting procedure; blurring?
Holly inlay properties
Divergence from the classic
Re: A small experiment
Re: A small experiment
Re: totes etc.
Re: Handle shaping method and tools... *LINK*
Re: A small experiment
Re: A small experiment
I used to get fired up...
The whole translation/review—for the obsessed *LINK*
Re: The whole translation/review—for the obsesse
Re: The whole translation/review—for the obsesse
Re: The whole translation/review—for the obsesse
Where is this going?
The purpose of the original test...
Re: The purpose of the original test...
What's allowed on forums?
you underestimate the interest
Re: you underestimate the interest
bored to tears ?
Re: bored to tears ?
There is one thing remaining..
My suspicion...
Re: My suspicion...
Re: My suspicion...
Another table from SB
Yes - the confusion without XHP
Odd thing about CTS-XHP wear resistance
All metal wear not equal
Re: This isn't Instagram
Re: This isn't Instagram
Re: The whole translation/review—for the obsesse
Re: not quite, but find what you like...
David - keep at it
Re: David - keep at it
Re: David - keep at it
I don't understand social media
© 1998 - 2017 by Ellis Walentine. All rights reserved.
No parts of this web site may be reproduced in any form or by
any means without the written permission of the publisher.

WOODCENTRAL, P.O. BOX 493, SPRINGTOWN, PA 18081