Hand Tools

Subject:
Re: Diamond wear
Response To:
Diamond wear ()

david weaver
I would be very surprised if someone gave you a CBN plane for a 1, 3 and 5 year period and you could tell that it was different than diamonds.

I have two plates that are all mono diamonds. One is DMT (or more accurately, I have two of each), and the other is atoma. The atoma plate has about 10x the use of the DMT and still works faster, even though it's technically finer. If Atoma did the same thing with CBN as they do with diamonds, I'm sure their plate would still outlast a duosharp.

Diamond loss and plating loss are a far bigger problem than wear.

No clue how material toughness plays into these, either, because it's not as if all diamonds are 70k knoop and all CBN is 45k. There are versions of CBN that are harder than typical diamonds, and arrangements of bonds in diamonds that make super hard diamonds (unlikely we see those - not sure about CBN).

At any rate, I'm going to have to hear stories about the CBN that wears down quickly before I think it's a big issue. I haven't got a clue what's made my atoma slower, but I'd imagine there may have been some initial diamond loss in the peaks. It still cuts very deeply with pressure. Or I should say both do, I have two and have lost track of which is which. AT one point, I saved one for stones, but I like them better once they've lost the initial tooth.

Still, on the CBN planes, it's not CBN that I'd be concerned about, it's flatness and the quality of attachment to the plate - as well as consistency of CBN if one has a choice. I already saw the damage a couple of stray large diamonds can do to a watch face.

Messages In This Thread

flattening Waterstones- shapton pro
Re: flattening Waterstones- shapton pro
Re: flattening Waterstones- shapton pro
Re: flattening Waterstones- shapton pro
Re: flattening Waterstones- shapton pro
Flattening
Revise atoma price...
Re: Revise dia-sharp price...
Diamond plates
Re: Diamond plates
Diamond plates......
Re: diasharp vs. diaflat
Re: diasharp vs. diaflat
Re: I think...
Re: I think...
Re: flattening Waterstones- shapton pro
Yes, this
lapping film?
Re: lapping film?
Re: lapping film?
you are not kidding!
Re: lapping film?
A different perspective *LINK*
Re: A different perspective
Not universal preference
to date
Re: to date
Re: to date
Re: to date
Re: to date
:) *NM*
Re: to date
Re: A different perspective
My Opinion...
Re: My Opinion...
My thoughts
Re: My thoughts
Re: My thoughts
The flat wheel surface - or not..
Re: The flat wheel surface - or not..
Re: The flat wheel surface - or not..
Re: The flat wheel surface - or not..
CBN and grit
How Are You Cleaning The CBN Wheel . . .
Re: How Are You Cleaning The CBN Wheel . . .
Re: How Are You Cleaning The CBN Wheel . . .
Why grind unhardened steel on CBN?
Re: Why grind unhardened steel on CBN?
Re: How Are You Cleaning The CBN Wheel . . .
Re: A different perspective
Re: flattening Waterstones- shapton pro
Quick and dirty summary:
Re: Quick and dirty summary:
Atoma - $64
Re: Atoma - $64
Sandpaper Flattening & Shaptons
Re: Sandpaper Flattening & Shaptons
Re: Sandpaper Flattening & Shaptons
Re: Sandpaper Flattening & Shaptons
Stearate coating
Re: Stearate coating
Re: Stearate coating
Re: Stearate coating
Plastic laminating sheet
Re: Stearate coating
which side to use?
Re: which side to use?
Re: which side to use?
Re: which side to use?
a little bit the Indian and a little bit arrow
Re: a little bit the Indian and a little bit arrow
What a great thread this has been.....
Re: What a great thread this has been.....
Re: What a great thread this has been.....
Re: What a great thread this has been.....
Traditional Method
Re: Traditional Method
Re: Traditional Method
Re: Traditional Method *LINK* *PIC*
Re: Traditional Method
Re: Traditional Method
Re: Traditional Method
Re: Traditional Method
Re: Traditional Method
Re: Traditional Method
Re: Traditional Method
Re: Traditional Method
Re: Traditional Method
Re: Traditional Method
My apologies for being a bit too harsh..
Re: Washita vs soft Arkansas stones...
Re: Washita vs soft Arkansas stones...
Re: Washita vs soft Arkansas stones...
Re: Washita vs soft Arkansas stones...
well then....
Another possibility presents itself......
CBN plates
Re: Not making sense..
Diamond wear
Re: Diamond wear
Re: Diamond wear
Re: Diamond wear
Re: Not making sense..
Re: Not making sense..
© 1998 - 2017 by Ellis Walentine. All rights reserved.
No parts of this web site may be reproduced in any form or by
any means without the written permission of the publisher.

WOODCENTRAL, P.O. BOX 493, SPRINGTOWN, PA 18081